1 epoxy sulfonated crosslinked anticorrosive paint

Product composition:

1 chlorosulfonated epoxy cross-linking type anticorrosive coating of chlorosulfonated polyethylene rubber, epoxy resin as basic material, join the antirust paint filler, stabilizing agent, curing agent, promoter, polyamide curing agent, organic solvent, etc of a two-component crosslinking type anticorrosive coating.

Product features:

Type 1 chlorosulfonated epoxy crosslinking integrates advantages of epoxy and chlorosulfonated polyethylene anticorrosion coating, quick drying, strong adhesion, high strength, compact structure of paint film, fullness is chlorosulfonated polyethylene film thickness, wet and heat resistance, salt fog resistance, heat resistance, weathering resistance, resistance to acid and alkali salt chemical corrosion medium, such as is an ideal material to chemical anticorrosive equipment.

Product use:

1 chlorosulfonated epoxy cross-linking type anticorrosive coatings are widely used in chemical industry, metallurgy, oil, ports, docks, Bridges, electricity and other equipment, pipeline, steel structure tower, concrete wall etc all the chemical atmospheric corrosion of equipment and facilities; Used for acid, alkali, salt storage tank inside and outside wall, urea, ammonium nitrate granule tower inside and outside wall, workshop, storage wall, floor and various chemical media corrosion equipment, etc.; Used for reservoir, cooling tower, sewage tank, water sluice, reservoir, etc.

Instructions:

Coating method: brush, roll, spray

Precoating: epoxy, chlorosulfonated polyethylene, high chlorinated polyethylene, epoxy sulfonated crosslinked primer

After coating: epoxy chlorine sulfonated crosslinked, chlorinated rubber modified chlorosulfonated, chlorinated rubber coatings

Coating number: two bottom two or two bottom three, dry film thickness of 150 microns.

Coating intervals: 23 + 2 ℃, the shortest 12 hours, the longest 24 hours

Technical indicators:

Appearance: primer: red, brown, light, flat and half light; Finish: colorful, semi-gloss.

Diluent: X-1 chlorosulfonated polyethylene coating thinner, X-7 epoxy paint thinner

Ratio: a: b = 10:1 (weight ratio)

Shelf life: 23 + 2 ℃ : 12 hours

Maturation period: 23 + 2 ℃ : 20 minutes

Drying time: 23 + 2 ℃ : table dry: 0.5 hours, work: 24 hours, fully cured 7 days.

Film thickness: 35 ~ 40 microns

Theoretical dosage: 180 ~ 200 g/m2

Packing specifications:

Iron bucket group a 20kg; The hydrated points 4 kg

Storage method:

Storage: must be stored in accordance with state regulations. The storage environment should be dry, cool, well ventilated, avoid high temperature and stay away from fire source. The packing container must be sealed.

Storage period: 12 months. After that, it should be checked and used.

Notes:

Safety: please pay attention to the safety items on the packing label. In addition, safety regulations set by relevant state or local governments should also be observed. Avoid long - term inhalation of solvent vapor or paint fog, skin, eyes must not contact this product, in the narrow place or the air is not in general construction, must provide strong ventilation, should wear good protective equipment during construction.

Note: this indicates that the data is obtained in the laboratory, which may vary slightly due to environmental conditions. The above data is subject to change without prior notice.