ZIRCONIA fused alumina
![Shop ZIRCONIA FUSED ALUMINA SAND-Detailed Image 1]()
Z Fused alumina was made from aluminum and Zirconium oxide by melting above 2250C in the electric arc furnace and cooling,
then the huge zirconia fused alumina lump is crushed into different sizes.
- T YPICAL CHEMICAL ANALISIS [%]
Items | Al2O3 | ZrO2 | TiO2 | Fe2O3 | SiO2 |
ZA25 | 68-72 | 24-30 | ≤1.5 | ≤0.5 | ≤1.0 |
ZA40 | 55-57 | 35-44 | ≤1.5 | ≤0.5 | ≤1.0 |
P HYSICAL PROPERTIES
Crystal Form | Monoclinic,tetragonal system |
Reaction with acid and alkali | no |
Reaction with carbon | Forming carbide since 1650C |
Color | Grey |
True Density | 4.20g/cm3 |
Bulk Density | 2.18g/cm3 |
Moh's hardness | 9.0 |
Knoop hardness | 1450-2000kg/cm2 |
Melting point | 1900C |
Maximum service temperature | 1700C |
Specific heat capacity(cal/g.C) | 0.2205(50-500C) |
Heat conductivity | 0.2718 cal/cm2.sec.C |
Linear expansivity(X10-6) | 6.82(100-700C) |
-
P ARTICLE SIZE DISTRIBUTION
F4 | +8000um | 0 | +5600um | ≤ 20% | +4750um | ≥4 0 % | +4750+4000um | ≥ 70% | -3350um | ≤3 % |
F5 | +6700um | 0 | +4750um | ≤ 20% | +4000um | ≥4 0 % | +4000+3350um | ≥ 70% | -2800um | ≤3 % |
F6 | +5600um | 0 | +4000um | ≤ 20% | +3350um | ≥4 0 % | +3350+2800um | ≥ 70% | -2360um | ≤3 % |
F7 | +4750um | 0 | +3350um | ≤ 20% | +2800um | ≥4 0 % | +2800+2360um | ≥ 70% | -2000um | ≤3 % |
F8 | +4000um | 0 | +2800um | ≤ 20% | +2360um | ≥4 5% | +2360+2000um | ≥ 70% | -1700um | ≤3 % |
F10 | +3350um | 0 | +2360um | ≤ 20% | +2000um | ≥4 5% | +2000+1700um | ≥ 70% | -1400um | ≤3 % |
F12 | +2800um | 0 | +2000um | ≤ 20% | +1700um | ≥4 5% | +1700+1400um | ≥ 70% | -1180um | ≤3 % |
F14 | +2360um | 0 | +1700um | ≤ 20% | +1400um | ≥4 5% | +1400+1180um | ≥ 70% | -1000um | ≤3 % |
F16 | +2000um | 0 | +1400um | ≤ 20% | +1180um | ≥4 5% | +1180+1000um | ≥ 70% | -850um | ≤3 % |
F20 | +1700um | 0 | +1180um | ≤ 20% | +1000um | ≥4 5% | +1000+850um | ≥ 70% | -710um | ≤3 % |
F22 | +1400um | 0 | +1000um | ≤ 20% | +850um | ≥4 5% | +850+710um | ≥ 70% | -600um | ≤3 % |
F24 | +1180um | 0 | +850um | ≤ 25% | +710um | ≥4 5% | +710+600um | ≥ 65% | -500um | ≤3 % |
F30 | +1000um | 0 | +710um | ≤ 25% | +600um | ≥4 5% | +600+500um | ≥ 65% | -425um | ≤3 % |
F36 | +850um | 0 | +600um | ≤ 25% | +500um | ≥4 5% | +500+425um | ≥ 65% | -355um | ≤3 % |
F46 | +600um | 0 | +425um | ≤ 30% | +355um | ≥4 0% | 355+300um | ≥ 65% | -250um | ≤3 % |
F54 | +500um | 0 | +355um | ≤ 30% | +300um | ≥4 0% | +300+250um | ≥ 65% | -212um | ≤3 % |
F60 | +425um | 0 | +300um | ≤ 30% | +250um | ≥4 0% | 250+212um | ≥ 65% | -180um | ≤3 % |
F70 | +355um | 0 | +250um | ≤ 25% | +212um | ≥4 0% | +212+180um | ≥ 65% | -150um | ≤3 % |
F80 | +300um | 0 | +212um | ≤ 25% | +180um | ≥4 0% | +180+150um | ≥ 65% | -125um | ≤3 % |
F90 | +250um | 0 | +180um | ≤ 20% | +150um | ≥4 0% | +150+125um | ≥ 65% | -106um | ≤3 % |
F100 | +212um | 0 | +150um | ≤ 20% | +125um | ≥4 0% | +125+106um | ≥ 65% | -75um | ≤3 % |
F120 | +180um | 0 | +125um | ≤ 20% | ≥4 0% | ≥4 0% | +106+90um | ≥ 65% | -63um | ≤3 % |
F150 | +150um | 0 | +106um | ≤ 15% | +75um | ≥4 0% | +75+63um | ≥ 65% | -45um | ≤3 % |
F180 | +125um | 0 | +90um | ≤ 15% | +75um | * | +75+63um | ≥ 40% | -53um | * |
F220 | +106um | 0 | +75um | ≤ 15% | +63um | * | +63+53um | ≥ 40% | -45um | * |
MAIN APPLICATIONS:
1. Making zircon fused alumina brick and building materials
2. Used for making bonded abrasives products,and process of grinding,sandblasting,surface treatment of metal products and other materials.
3. With good melt erosion resistance,Zirconia fused alumina has good grinding effect on steel,iron casting,heat resistant steel and other alloy materials.
4. Zirconia fused alumina can be made for heavy duty Zirconia fused alumina grinding wheel,snagging,cutting disc,Fiber disc,grinding rails,high speed abrasive belts etc
5. Used for making coated abrasives products,
6. Used for making lapping paste,polishing wax,emery cloth,sandpaper etc
7. ZA is primarily used for steel conditioning wheels, snagging wheels, large diameter cut-offs and other grinding applications that require high speed and pressure. It's also is recommended for refractories that require a high resistance to environmental corrosion and a low coefficient of thermal expansion. Applications include slide gates, glass tank refractories, and other applications requiring resistance to molten slags.