Epoxy low-zinc workshop anticorrosive paint 70%

Composition:

Epoxy low - zinc workshop anticorrosive paint consists of epoxy resin, super fine zinc powder, aluminum powder, polyamide resin, solvents and additives.

Main features:

Epoxy anticorrosive paint zinc powder content is low zinc workshop half of zinc rich primer, as long as the film thickness within the prescribed scope, does not affect the welding performance, but when the welding cutting can greatly reduce the harmful gas. The paint film still has the cathodic protection function, has the good anti-rust property, the dry quick, only very short time is able to carry, pile up and the paint after coating; Adapt to the requirements of steel pretreatment assembly line; The paint film has good adhesion and can be compatible with most paint systems.

Product use:

The anticorrosive coating of epoxy low-zinc workshop is suitable for the pretreatment of steel structures such as shipyard and heavy machinery plant for workshop maintenance. The maintenance period is more than 4 months.

Instructions:

Coating method: hand brush, roller coating, high-pressure airless spraying

Film thickness: wet film: 90 micron; Dry film: 25 microns

After coating: chlorinated rubber, epoxy, asphalt, epoxy ester, chlorosulfonated polyethylene coating.

Coating number: high pressure airless spray, dry film thickness of 25 mu m.

Coating intervals: 23 + 2 ℃, minimum 24 hours

Technical indicators:

Appearance: primers red, semi-gloss; Paint all colors, smooth

Flash: 26 ℃

Diluent: x-12 organic silicon anticorrosive paint special diluent

Density: primer about 1.2; Paint is about 1.15

Drying time: 23 + 2 ℃ : table dry for 1 hour or less, work 24 hours or less, completely curing 7 days theory usage: 90 g / ㎡ primer; Paint 80 g / ㎡

Film thickness: wet film: primer 70 mu m; Paint 60 mu m; Dry film: primer 30 mu m; Finish 25 microns.

Packing specification: iron bucket 20L 20kg

Storage method:

Storage: must be stored in accordance with state regulations. The storage environment should be dry, cool, well ventilated, avoid high temperature and stay away from fire source. The packing container must be sealed.

Storage period: 12 months. After that, it shall be used after passing inspection.

Notes:

Safety: the construction site should have good ventilation condition, prevent solvent gas and spray paint mist inhalation. Note: products should be kept away from heat source. Smoking should be strictly prohibited in construction site. This manual is prepared according to the knowledge and experience gained in our laboratory and construction practice, but the coating construction process is usually outside the control of our company.